C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
≤0.035 |
≤0.075 |
≤ 2.00 |
≤0.04 |
≤0.03 |
18.00-20.00 |
3.00-4.00 |
11.00-15.00 |
Chemical Composition
Mechanical Properties
Tensile Strength ksi (Mpa) |
Yield Strength ksi (Mpa) |
Elongation -% in 50 mm |
Hardness (Brinell) |
Hardness Rockwell |
≥75(515) |
≥30(205) |
≥35 |
≤ 192HBW/200HV |
≤ 90HRB |
Applications
Grade 317L is commonly used to handle sulfur, pulp liquor, acid dyestuffs, acetylating and nitrating mixtures, bleaching solutions, severe coal and oil, and many chemical compounds. Some other applications that use 317L include:
- Paper and pulp handling equipment
- Chemical and petrochemical processing equipment
- Condensers in fossil and nuclear fueled power generation stations
- Food processing equipment
- Textile equipment
Testing
- EN 10204/3.1B, EN 10204 3.1 and EN 10204 3.2 Material Test Certificates (MTC)
- Raw Materials Certificate
- 100% Radiography Test Report
- 100% PMI
- Heat Treatment Charts
- Third Party Inspection Report
- Surface roughness and size measurement
- Manufacturer Test Certificate( Impact Testing, Flatten, Spin,Curve, Hardness, Intergranular ,Point corrosions, Grain size, ET,UT, HT...)
- Laboratory Test Certificate from Govt. Approved Lab
- ......
End of Pipe and Tube
- BE : Beveled end
- BBE : Bevel both ends
- BLE : Bevel large end
- BSE : Bevel small end
- TOE / POE = Treaded One End / Plain One End
- TOE / BOE = Treaded One End / Beveled One End
- POE / BOE = Plain One End / Beveled One End
- TBE = Treaded Both Ends
- PBE = Plain Both Ends
Packing
- Ply Wooden Boxes
- PE Fabric Bundles
- Standard seaworthy export packing
- Plastic Bags, or as required
Marking
- Supplier / Manufacturer Name or Custom Logo - on request
- Specification
- Material Grade
- Nominal Size
- Schedule or Wall Thickness
- Method of Manufacturing (Seamless or Welded)
- Heat Number
Marked Pipe Sample: XTD ASTM A312 TP317L SEAMLESS 42.2x 3.56*6000MM HEAT NO. 2023121205A15
Material Summary
317L (UNS S31703) is a low carbon corrosion resistant austenitic chromium-nickel-molybdenum stainless steel. The high levels of these elements assure the steel has superior chloride pitting and general corrosion resistance to the conventional 304/304L and 316/316L grades. The steel provides improved resistance relative to 316L in strongly corrosive environments containing sulfurous media, chlorides, and other halides.
The low carbon content of 317L enables it to be welded without intergranular corrosion resulting from chromium carbide precipitation enabling it to be used in the as-welded condition.
The grade 317L is non-magnetic in the annealed condition. It cannot be hardened by heat treatment; however the material will harden due to cold working. 317L can be easily welded and processed by standard shop fabrication practices.