SA-213/SA-213M Specification for seamless Ferritic Alloy steel boiler, Superheater and heat exchanger tubes
Delivery Condition:
Normalized and Tempered
Inspections and Tests Performed: Chemical Composition Inspection, Mechanical
Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring,
Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test,
No-destructive Test, Hydrostatic Test.
Surface treatment: Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting
Inner packing: Caps on two ends of every pipe
Package: bare packing/bundle packing/wooden carton packing.
|
Size Tolerance |
||||
|
Tube Kinds |
SA213 OD（D） |
SA213 Thickness（S） |
||
|
OD（mm） |
OD Tolerance（mm） |
OD（mm） |
Thickness Tolerance（mm） |
|
|
Hot Rolled |
≤101.6 |
+0.4～-0.8 |
76～168.3 |
+28%～0 |
|
>101.6～168.3 |
+0.4～-1.2 |
|||
|
Cold Drawn |
<25.4 |
0.1 |
≤38.1 |
+20%～0 |
|
25.4～38.1 |
0.15 |
|||
|
>38.1～<50.8 |
0.2 |
>38.1 |
+22%～0 |
|
|
50.8～<63.5 |
0.25 |
|||
|
63.5～<76.2 |
0.3 |
|||
|
76.2～101.6 |
0.38 |
|||
|
>101.6～190.5 |
+0.38～-0.64 |
|||
|
>190.5～228.6 |
+0.38～-1.14 |
|||
|
Grade |
Tensile Strength,Min., ksi[MPa] |
Yield Strength,Min., ksi[MPa] |
Elongation |
|
T12 |
60 [415] |
32 [220] |
30 |
|
T23 |
74 [510] |
58 [400] |
20 |
|
T91 |
85 [585] |
60 [415] |
20 |
|
T92 |
90 [620] |
64 [440] |
20 |
|
T122 |
90 [620] |
58 [400] |
20 |
|
18Cr-2Mo |
60 [415] |
40 [275] |
20 |
|
NOTES: |
|
|
|
|
(1) When standard round 2 in. or 50 mm gage length or smaller proportionally sized specimens with gage length equal to 4D (4 |
|||
|
times the diameter) is used, the minimum elongation shall be 22% for all ferritic grades except 18Cr-2Mo, T23 and T91. |
|||
|
(2) For longitudinal strip tests, a deduction from the basic minimum |
|
||
|
CHEMICAL REQUIREMENTS FOR FERRITIC STEEL |
||||||||||
|
Composition, % |
||||||||||
|
Grade |
Carbon |
Manganese |
Phosphorus, Max. |
Sulfur, Max |
Silicon |
Chromium |
Molybdenum |
Titanium |
Vanadium,Min. |
Other Elements |
|
T2 [Note (1)] |
0.10–0.20 |
0.30–0.61 |
0.025 |
0.025 |
0.10–0.30 |
0.50–0.81 |
0.44–0.65 |
. . . |
. . . |
|
|
T5 |
0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
0.50 max. |
4.00–6.00 |
0.45–0.65 |
. . . |
. . . |
|
|
T5b |
0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
1.00–2.00 |
4.00–6.00 |
0.45–0.65 |
. . . |
. . . |
|
|
T5c |
0.12 max. |
0.30–0.60 |
0.025 |
0.025 |
0.50 max. |
4.00–6.00 |
0.45–0.65 |
[Note (1)] |
. . . |
|
|
T9 |
0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
0.25–1.00 |
8.00–10.00 |
0.90–1.10 |
. . . |
. . . |
|
|
T11 |
0.05 min.–0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
0.50–1.00 |
1.00–1.50 |
0.44–0.65 |
. . . |
. . . |
|
|
T12 [Note (1)] |
0.05 min.–0.15 max. |
0.30–0.61 |
0.025 |
0.025 |
0.50 max. |
0.80–1.25 |
0.44–0.65 |
. . . |
. . . |
|
|
T17 |
0.15–0.25 |
0.30–0.61 |
0.025 |
0.025 |
0.15–0.35 |
0.80–1.25 |
. . . |
. . . |
0.15 |
|
|
T21 |
0.05 min.–0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
0.50 max. |
2.65–3.35 |
0.80–1.06 |
. . . |
. . . |
|
|
T22 |
0.05 min.–0.15 max. |
0.30–0.60 |
0.025 |
0.025 |
0.50 max. |
1.90–2.60 |
0.87–1.13 |
. . . |
. . . |
|
|
T23 |
0.04–0.10 |
0.10–0.60 |
0.03 |
0.01 |
0.50 max. |
1.90–2.60 |
0.05–0.30 |
. . . |
0.20–0.30 |
W 1.45–1.75 |
|
T91 |
0.08–0.12 |
0.30–0.60 |
0.02 |
0.01 |
0.20–0.50 |
8.00–9.50 |
0.85–1.05 |
. . . |
0.18–0.25 |
Cb 0.06–0.1 |
|
T92 |
0.07–0.13 |
0.30–0.60 |
0.02 |
0.01 |
0.50 max. |
8.50–9.50 |
0.30–0.60 |
. . . |
0.15–0.25 |
W 1.5–2.00 |
|
T122 |
0.07–0.14 |
0.70 max. |
0.02 |
0.01 |
0.50 max. |
10.00–12.50 |
0.25–0.60 |
. . . |
0.15–0.30 |
W 1.50–2.50 |
|
18Cr-2Mo |
0.025 max. |
1.00 max. |
0.04 |
0.03 |
1.00 max. |
17.5–19.5 |
1.75–2.50 |
[Note (3)] |
. . . |
N max. 0.035 |
|
NOTES: |
|
|
|
|
|
|
|
|
|
|
|
(1) It is permissible to order T2 and T12 with 0.045 max. Sulfur. |
||||||||||
|
(2) Grade T5c shall have a titanium content of not less than four times the carbon content and not more than 0.70%. |
||||||||||
|
(3) Grade 18Cr-2Mo shall have Ti + Cb p 0.20 + 4 (C + N) min., 0.80 max. |
||||||||||