ASTM A335 P11 Alloy Steel Seamless Pipes and Tubes

ASTM A335 P11 Alloy Steel Seamless Pipes and Tubes

ASTM A335 P11 Alloy Steel Seamless Pipes and Tubes

① Size: 50.8 to 860 mm

② Wall Thickness: 2.77 to 100mm

③ Shape: Round

④ Length: Single random length/ Double random length or as customer’s actual request

⑤ Grade: P11, P12, P22, P91


Introduction

ASTM A335 /A335M ASME SA335 pipes shall be made by the seamless process and shall be either hot-finished or cold drawn with the finishing treatment.

ASTM A335 /A335M covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high-temperature service.

Referenced Documents

ASTM A 999/A999M specification for general requirements for alloy and stainless-steel pipe
E92 Test method for Vickers hardness of metallic materials
E213 practice for ultrasonic testing of metal pipe and tubing
E309 practice for Eddy-Current examination of steel tubular products using magnetic saturation
E381 method of macro etch testing steel bars, billets, blooms, and forgings

Chemical Composition

Grade C Mn P S Si Cr Mo V Nb N Al others
P11 0.05-0.15 0.30-0.60 ≤0.025 ≤0.025 0.50-1.00 1.0-1.50 0.44-0.65 / / / / /
P12 0.05-0.15 0.30-0.61 ≤0.025 ≤0.025 ≤0.50 0.80-1.25 0.45-0.65 / / / / /
P22 0.05-0.15 0.30-0.60 ≤0.025 ≤0.025 ≤0.50 1.90-2.60 0.87-1.13 / / / / /
P91 0.08-0.12 0.30-0.60 ≤0.020 ≤0.010 0.20-0.50 8.0-9.50 0.85-1.05 0.18-0.25 0.030-0.070 ≤0.40 ≤0.02
Cb 0.06-0.10
Ti 0.01max
Zr 0.01max

Chemical Composition
Heat Treatment Requirements

Grade

P11

P12

P22

P91

UNS Number

K11597

K11562

K21590

K91560

Heat Treat Type

full or isothermal anneal normalize and temper

full or isothermal anneal normalize and temper subcritical anneal

full or isothermal anneal normalize and temper

normalize and temper

quench and temper

Austenitizing/ Solutioning

Temperature, min or range °F [°C]

1900-1975[1040-1080]

1900-1975[1040-1080]

Subcritical Annealing or Tempering

Temperature, Min or range °F [°C]

1200 [650]

1200 [650]

1200-1300 [650 to 705]

1250 [675]

1350-1470[730-800]

1350-1470[730-800]

Tensile Requirements and Hardness

Grade

Tensile

Yield

Elongation

Hardness

Strength (Mpa)

Strength (Mpa)

(%)


P11 P12

≥415

≥220

≥30

≤89HRB

P22

≥415

≥200

≥30

≤89HRB

P91

≥585

≥415

≥20

91HRB-25HRC

If you have any enquiry about quotation or cooperation,please feel free to email us at or use the following enquiry form. Our sales will contact you within 24 hours. Thank you for your interest in our products.

We value your privacy

We use cookies to enhance your browsing experience, serve personalized ads or content, and analyze our traffic. By clicking "Accept All", you consent to our use of cookies.

Consent Preferences

Consent Preferences